Low Force Shrink Film

Low Force Shrink Film

It is low force shrink film, which can help soft and elastic proudcts keeping good impact, without distortion. The shrink force is small enough that it can pack soft objects easily, while the strength is big enough that it is suitable for odd shape items. As JT05 can provide tight packing on odd shape items, the performance keeps glossy and without wrinkle. JT05 can pack heat sensitive items due to its low temperature shinking feature. This soft shrink film is designed for showcase items such as books, magazines, computer manuals, or converted paper products .

Features: 1.low shrink force; 2.Extremely wide operating window; 3.Great shrinkage; 4.Low sealing and shrink temperature.

Available thickness: 15micron, 19micron


JT05 Low Force Shrink Film
TEST ITEM UNIT ASTM TEST TYPICAL VALUES
THICKNESS     12um 15um 19um 25um
TENSILE
Tensile Strength (MD) N/mm2 D882 76 71 71 66
Tensile Strength (TD) 66 61 61 61
Elongation (MD) % 106 106 111 111
Elongation (TD) 86 91 91 96
TEAR
MD g D1922 15.6 18.6 32.1 40.1
TD 13.6 16.6 23.6 30.1
SEAL STRENGTH
MD/Hot Wire Seal N/mm F88 0.78 0.88 1.05 1.35
TD/Hot Wire Seal 0.72 0.82 1.01 1.27
COF(film to Film)
Dynamic   D1894 0.31 0.28 0.27 0.31
Static   0.32 0.29 0.28 0.32
Static (Hot Slip) @ 60℃   0.39 0.37 0.36 0.35
OPTICS
Haze   D1003 3.2 3.7 4.3 4.6
Clarity   D1746 97.6 98.1 97.1 95.1
Gloss @ 45Deg   D2457 86.6 84.1 82.1 80.6
BARRIER
Oxygen Transmission Rate cc/m2/day D3985 12300 11200 9400 6200
Water Vapor Transmission Rate gm/m2/day F1249 50 43 36 29
SHRINKAGE PROPERTIES MD TD MD TD
Free Shrinkage 80℃ % D2732 24 21 22 18
90℃ 30 33 28 27
100℃ 51 53 49 48
110℃ 60 61 56 57
120℃ 66 66 64 66
130℃ 71 69 69 68
Shrink Tension 90℃ Mpa D2838 1.70 1.80 1.80 1.85
100℃ 1.90 2.00 2.05 2.15
110℃ 2.05 2.10 2.25 2.30
120℃ 1.85 1.95 2.00 2.05
Note: This infor mation represents our best judgment on the work done,but the company assumes no liability whatsoever in connection with the use of infomation or findings contained herein.