Hot Slip Shrink Film

Hot Slip Shrink Film

JT02 Its main advantage is excellent hot slip property. When the film without hot slip property, the hot surface after shrink causes stick, which makes you put the packs together hard. JT02 is your best choice to avoid such difficulities. Except for hot slip property, it has all good properties of JT01.

Available thickness: 12micron, 15micron, 19micron, 25micron and 30 micron.


JT02 Hot Slip Shrink Film
TEST ITEM UNIT ASTM TEST TYPICAL VALUES
THICKNESS     12um 15um 19um 25um
TENSILE
Tensile Strength (MD) N/mm2 D882 111 111 106 91
Tensile Strength (TD) 106 106 101 86
Elongation (MD) % 111 116 121 126
Elongation (TD) 106 111 111 121
TEAR
MD g D1922 11.1 14.1 16.1 24.1
TD 9.6 12.1 15.1 22.1
SEAL STRENGTH
MD/Hot Wire Seal N/mm F88 0.78 0.93 1.20 1.30
TD/Hot Wire Seal 0.81 0.95 1.18 1.43
COF(film to Film)
Dynamic   D1894 0.29 0.27 0.26 0.29
Static   0.30 0.28 0.27 0.30
Static (Hot Slip) @ 60℃   0.37 0.36 0.35 0.33
OPTICS
Haze   D1003 2.4 2.9 3.7 4.2
Clarity   D1746 97.3 96.6 96.1 95.1
Gloss @ 45Deg   D2457 86.1 84.1 83.6 82.1
BARRIER
Oxygen Transmission Rate cc/m2/day D3985 11800 11000 8500 6700
Water Vapor Transmission Rate gm/m2/day F1249 48.6 37.6 28.7 23.6
SHRINKAGE PROPERTIES MD TD MD TD
Free Shrinkage 100℃ % D2732 21 30 21 27
110℃ 39 44 36 46
120℃ 59 62 57 61
130℃ 66 67 65 66
Shrink Tension 100℃ Mpa D2838 1.80 2.65 1.95 2.75
110℃ 2.70 3.50 2.80 3.55
120℃ 2.90 3.65 2.95 3.75
130℃ 2.65 3.35 2.75 3.40
Note: This infor mation represents our best judgment on the work done,but the company assumes no liability whatsoever in connection with the use of infomation or findings contained herein.